Magnesium Fluoride (MgF2)
 
Magnesium Fluoride is used for optical elements in both the infrared and ultraviolet. Its useful transmission range is from 0.19µm; to 6.5µm. The refractive index varies from about 1.48 to 1.3. Magnesium Fluoride is a bi-refringence material and this aspect should be taken into consideration before selection of this material in an optical design. Janos uses only VUV grade material, with the C-axis oriented to minimize birefringence. Irradiation does not lead to color centers. This VUV material is the least susceptible to radiation induced color centers.
Magnesium Fluoride is one of the lowest index infrared materials, second only to Lithium Fluoride. It is resistant to thermal and mechanical shock. The material is twice as hard as Calcium Fluoride but only half as hard as Germanium. Magnesium Fluoride is significantly more expensive than Calcium Fluoride and Barium Fluoride, but usually not more expensive than Lithium Fluoride. Magnesium Fluoride is similar to Calcium Fluoride in its resistance to water.
 
Property
Specification
Transmission Range
0.121µm to 7.0µm
Density
3.177 g/cm3
Thermal Expansion
13.7 x 10-6 /°C Parallel to C-axis
Co-Efficient
8.48 x 10-6 /°C Perpendicular to C-axis
Surface Finish
Polishes of 10-5, or 20-10 scratch-dig are achieved at extra costs respectively mainly for UV applications. Typical specifications for surface quality in the visible & near infrared regions are a 40-20 & 60-40 scratch dig in the 3 to 7µm range. MgF2 is diamond turnable.
Surface Figure
In the UV & Visible spectral regions, surface figure ranges from 1/10 wave to 1/2 wave @ 0.6328µm. In the infrared, typical required surface figure ranges from 1/2 wave to 2 waves @ 0.6328µm & are specified depending on the system performance requirements.
AR Coating Options
Magnesium Fluoride can be AR coated for use in the infrared but generally without much improvement in transmission due to its low index of refraction & already high transmission.
Typical Applications
Thermal imaging, Astronomical, Excimer laser applications.
Products Manufactured
Lenses, Aspheric lenses, Windows, Optical Beamsplitters, Optical Filters, Wedges, Prisms.
 
Wavelength (µm)
Index of Refraction (n)
0.114
1.7805
0.118
1.6800
0.130
1.5560
0.150
1.4800
0.170
1.4470
0.190
1.4310
0.300
1.4000
0.700
1.3760